Mechanische Eigenschaften
Brass has different mechanical properties due to different zinc content. Fig. 7 is a graph showing the change of mechanical properties of brass with different zinc content. For brass, σb and δ increase with the increase of zinc content. For ( plus ) brass, the strength at room temperature increases continuously before the zinc content increases to about 45 percent . If the zinc content is further increased, the R phase with greater brittleness (solid solution based on Cu5Zn8 compound) appears in the alloy structure, and the strength decreases sharply. The room temperature plasticity of ( plus ) brass always decreases with the increase of zinc content. Therefore, the copper-zinc alloy containing more than 45 percent zinc has no practical value.
Gewöhnliches Messing wird häufig verwendet, z. B. für Wassertankriemen, Wasserversorgungs- und Abflussrohre, Medaillen, Wellrohre, Serpentinenrohre, Kondensatorrohre, Schalengehäuse, verschiedene komplexe gestanzte Produkte, Hardware und so weiter. Mit der Erhöhung des Zinkgehalts von H63 auf H59 können sie der Heißverarbeitung gut standhalten und werden hauptsächlich in verschiedenen Teilen von Maschinen und Elektrogeräten, Stanzteilen und Musikinstrumenten verwendet.
Um die Korrosionsbeständigkeit, Festigkeit, Härte und Bearbeitbarkeit von Messing zu verbessern, wird eine geringe Menge an Elementen wie Zinn, Aluminium, Mangan, Eisen, Silizium, Nickel, Blei usw. (im Allgemeinen 1 Prozent 2 Prozent, einige bis zu 3 Prozent, 4 Prozent und einige bis zu 5 Prozent) werden der Kupfer--Zink-Legierung zugesetzt, um ternäre, quaternäre oder sogar quinäre Legierungen zu bilden, was sehr komplex ist
Zink-Äquivalentkoeffizient
The microstructure of complex brass can be calculated according to the "zinc equivalent coefficient" of elements added in brass. Because a small amount of other alloying elements are added to Cu-Zn alloy, the /( plus ) phase region in Cu-Zn state diagram usually moves to the left or right. Therefore, the microstructure of special brass is usually equivalent to that of ordinary brass with increased or decreased zinc content. For example, the microstructure of Cu-Zn alloy with 1 percent silicon is equivalent to the alloy structure with 10 percent zinc added in Cu-Zn alloy. So the "zinc equivalent" of silicon is 10. The "zinc equivalent coefficient" of silicon is the largest, which makes the /( plus ) phase boundary in Cu-Zn system significantly move to the copper side, that is, the phase region is strongly reduced. The "zinc equivalent coefficient" of nickel is negative, that is, the phase region is enlarged.
Die --Phase und --Phase in Sondermessing sind komplexe Multi--Mischkristalle, die eine große Festigungswirkung haben, während die --Phase und --Phase gewöhnliches Messing sind einfache Cu--Mischkristalle, die eine geringe Verstärkungswirkung haben. Obwohl das Zinkäquivalent äquivalent ist, sind die Eigenschaften von Mehrkomponenten-Mischkristallen und einfachen binären Mischkristallen unterschiedlich. Daher ist eine kleine Menge an Multi--Verstärkung eine Möglichkeit, die Legierungseigenschaften zu verbessern.